metal stitching process Archives - Metal Stitching and Metal Locking Services

Engine Block | Cylinder Liner | Crack Repair – RA Power Solutions

By RAPowerSolution |

Crack repair of heavy components is undertaken onsite by RA Power Solutions having more than 44 Years of experience. The heavy cast components, which get seriously damaged into multiple pieces, are repaired by preparing a new piece of Casting and Metal locking/Metal Stitching process. The repair of seriously damaged cast components and cracks is executed […]

Crack Repair Of Aluminium | Bronze And Cast Iron Component By Metal Lock & Metal Stitching

By RAPowerSolution |

RA Power Solutions is one of the oldest companies based in New Delhi, India, undertaking crack repairs of damaged heavy components, manufactured out of cast iron, bronze, aluminium, and cast steel by cold process of metal lock and metal stitching. Metal stitching and metal locking is a simple but proven process of repairing cracks in […]

Cast Iron Repair | Aluminum | Bronze Crack Repair | Metal Lock | Metal Stitching

By RAPowerSolution |

Metal lock & metal stitching is the process by which cracks or damaged broken cast iron, bronze, and aluminum components can be repaired. We have been extending services for metal locking and metal stitching for turbine-generating equipment, large water pumps, forging equipment and various components of high-capacity diesel-generating sets. All these years we have been […]

Metal Locking | Metal Stitching | Crack Repair Damaged Casting Rectification | Ra Power Solutions

By RAPowerSolution |

RA Power Solutions has recently undertaken repair of the centre fuse rear casing machine block of a fertilizer plant in Northern India. The problem of heavy leakage of oil was observed from the rear centre fuse casing. Our technicians visited the site and carried out the following jobs. Action taken for repair of damaged centre […]

Metal Stitching & Metal Locking Of Engine Block

By RAPowerSolution |

RA Power Solutions has been undertaking the repair & maintenance of heavy equipment in industries, power plants and diesel engines installed on the vessel for the last more than 4 decades. We have experienced that in spite of following the rigid maintenance schedule mentioned in the maintenance manual of the manufacturer, serious accidents do take […]

Cast Iron Aluminium Crack Repair | Cracked Aluminium Cylinder Head Repair

By RAPowerSolution |

Gone are the days when in case of cracks in aluminium cast components were rejected and replaced by new ones as it was not possible to undertake the crack repair in aluminium cast components or the components which used to get damaged due to accidents. The welding process in some cases was used for aluminium […]

Onsite Crack Repair | Metal Lock | Metal Surgery

By RAPowerSolution |

It is surprising, but it is the fact that the repair of cracks and repair of damaged components manufactured out of cast iron, aluminium and cast steel are successfully repaired by metal lock and metal surgery process. This process of Onsite Crack Repairhas replaced the old and conventional method of repair of cracks by welding. […]

CRACK REPAIR BY METAL STITCHING INSTEAD OF WELDING

By RAPowerSolution |

Metal stitching is a technology which is over 100 years old and now very well proven and established to undertake crack repair or damage to cast components manufactured out of cast iron or aluminium alloy. In some cases, crack repair is also possible in components made of bronze. RA Power Solutions as a repair company […]

CRACK REPAIR IN ENGINE BLOCK | REPAIR OF DAMAGE CASTING

By RAPowerSolution |

In the case of high high-capacity engine, it is difficult to replace the engine block due to the development of cracks or serious damage to the block. The engines which are installed in diesel power plants and heavy engineering industry can still be transported to designated workshops for necessary repairs but in the case of […]

CRACK REPAIR OF LARGE CAST IRON COMPONENT

By RAPowerSolution |

Accidents in the case of rotatory equipment are common. Again, it is observed that in the case of stationary heavy-duty machinery parts made out of cast iron or cast steel, cracks develop due to fatigue, casting defects, or mechanical failures. The misalignment of components, excessive vibration, or overload can also be one of the causes […]