Metal Stitching and Metal Locking Archives - Metal Stitching and Metal Locking Services

Crack Repair Of Aluminium | Bronze And Cast Iron Component By Metal Lock & Metal Stitching

By RAPowerSolution |

RA Power Solutions is one of the oldest companies based in New Delhi, India, undertaking crack repairs of damaged heavy components, manufactured out of cast iron, bronze, aluminium, and cast steel by cold process of metal lock and metal stitching. Metal stitching and metal locking is a simple but proven process of repairing cracks in […]

Cylinder Liner | Engine Block | Crack Repair Of Man Main Engine | Metal Lock And Metal Stitching

By RAPowerSolution |

RA Power Solutions was informed about a serious accident on a vessel damaging SMIT MAN R666W (Main Engine). The cylinder liner and Engine block housing developed multiple cracks. Two technicians having experience of 44 years in crack repair by metal stitching and metal locking were deputed on board a vessel. The following are the main […]

Cast Iron Cylinder Head Repair | Cast Iron Head Repair

By RAPowerSolution |

Cast Iron Cylinder Head Repair At RA Power Solutions, we fix broken engine parts called cylinder heads. Imagine a cylinder head like a cap on a bottle- it keeps everything inside safe. Sometimes, these cylinder heads, made of strong cast iron, can get damaged. That’s where we come in! Our experts at RA Power Solutions […]

Metal Stitching & Metal Locking Of Engine Block

By RAPowerSolution |

RA Power Solutions has been undertaking the repair & maintenance of heavy equipment in industries, power plants and diesel engines installed on the vessel for the last more than 4 decades. We have experienced that in spite of following the rigid maintenance schedule mentioned in the maintenance manual of the manufacturer, serious accidents do take […]

Crack Repair Process For Aluminium | Bronze And Aluminium Components | Ra Power Solutions

By RAPowerSolution |

It is proven that crack repair in cast iron, bronze and aluminium heavy components by metal lock and metal stitching process is a highly successful and proven way of undertaking the repairs. In crack repair or badly damaged cast iron by metal lock and metal stitching method, no heat is generated as it is a […]

Cast Iron Repair | Broken Engine Block by Metal Stitching

By RAPowerSolution |

RA Power Solutions was called by a client based in the Maldives to inspect the engine block of Wartsila 12V32 which got seriously damaged due to an accident. RA Power Solutions technicians visited the island and undertook the inspection as per the following details: The details of the crack observed are as follows:- Non-availability of […]

Onsite Crack Repair | Metal Lock | Metal Surgery

By RAPowerSolution |

It is surprising, but it is the fact that the repair of cracks and repair of damaged components manufactured out of cast iron, aluminium and cast steel are successfully repaired by metal lock and metal surgery process. This process of Onsite Crack Repairhas replaced the old and conventional method of repair of cracks by welding. […]

Crack Repair In Cast Iron | Aluminium | Cast Steel

By RAPowerSolution |

RA Power Solutions has made repair of cracks and damaged engine blocks a simple process. This achievement of repairing engine block, turbine casing, Cylinder heads, and major parts of high-capacity engines is possible because of our experience in undertaking repairs of damage and crack casting by metal lock and metal stitching process. The cast iron […]

CRACK REPAIR BY METAL STITCHING INSTEAD OF WELDING

By RAPowerSolution |

Metal stitching is a technology which is over 100 years old and now very well proven and established to undertake crack repair or damage to cast components manufactured out of cast iron or aluminium alloy. In some cases, crack repair is also possible in components made of bronze. RA Power Solutions as a repair company […]

CRACK REPAIR OF LARGE CAST IRON COMPONENT

By RAPowerSolution |

Accidents in the case of rotatory equipment are common. Again, it is observed that in the case of stationary heavy-duty machinery parts made out of cast iron or cast steel, cracks develop due to fatigue, casting defects, or mechanical failures. The misalignment of components, excessive vibration, or overload can also be one of the causes […]