RA Power Solutions have made repair of crack and damaged engine block a simple process. This achievement of repairing engine block, turbine casing, Cylinder heads and major parts of high capacity engines is possible because of our experience in undertaking repairs of damage and crack casting by metal lock and metal stitching process.
The cast iron engine block is difficult to weld as it is very brittle. The repair of the crack engine block by metal lock/metal stitching/metal surgery is proven to be of great success and can result in saving a huge amount as one can avoid buying a new engine block.
Repair of Wartsila 12V32 engine block
One of our client running a Diesel power plant in south America having 47 numbers of Wartsila 12V32 and Wartsila 18V32 engines reported serious accident of one of their diesel generating sets of Wartsila 12V32 model. The team of engineers of RA Power Solutions conducted the inspection and following observations were made:-
- The accident took place due to failure of connecting rod bearing. The connecting rod hit the engine block from both the sides and damaged the block. On undertaking the crack detection test by MPI and die-penetrant test multiple cracks having length measuring from 3 inches to 18 inches were observed.
Following action was taken to repair Wartsila Engine block:-
- It was decided to cut the damage and crack portion of the engine block and give it a discipline profile.
- The portion measuring 24 inches by 39 inches and 13 inches by 26 inches on both sides of the engine block was removed.
- The MPI test was conducted to ensure that no cracked area remains in the crankcase.
- The wooden pattern was prepared onsite as per the damaged and removed casting portion of the engine block. The new casting was manufactured strictly as per the wooden pattern dimensions and profile and necessary machining was done in house.
- The new casting was placed on the engine block and was attached by metal locking and metal stitching process by our technicians.
- The outer surface was ground and was matched with the parent casting.
- The repair of engine block by replacing the damage casting and fixing it by metal lock and metal stitching proved to be successful.
- Our technicians also ensured that no leakage of lubricating oil takes place.
RA Power Solutions Pvt. Ltd. have been extending the repair of crack and damage casting services for the last forty years and have the technicians and necessary portable tooling available to undertake the onsite repairs. The repairs on board the vessel and while sailing of the vessel is also possible. We have the technicians possessing Indian CDC and it is possible to depute them in a short notice.
Follow up by RA Power Solutions after repair of Wartsila engine 12V32 was done and it was communicated that the Engine have completed more than 6300 running hours after repair. No leakages and no problem in the operation has been reported.
The company have saved an enormous amount by avoiding the purchase of a new engine block from Wartsila.