Metal Stitching and Metal Locking Archives - Page 2 of 2 - Metal Stitching and Metal Locking Services

Crack Repair Process For Aluminium | Bronze And Aluminium Components | RA Power Solutions

By RA Power Solutions |

Engineers have successfully repaired cracks in heavy cast iron, bronze, and aluminium components using metal locking and metal stitching. The process provides a reliable method for restoring damaged castings without applying heat. Because metal stitching and metal locking use a cold repair process, they do not generate heat or introduce thermal stress into the component […]

Cast Iron Repair | Broken Engine Block by Metal Stitching

By RA Power Solutions |

A client based in the Maldives contacted RA Power Solutions to inspect a Wärtsilä 12V32 engine block that had suffered severe damage in an accident. RA Power Solutions technicians visited the island and undertook the inspection as per the following details: The details of the crack observed are as follows: – Repairing a Damaged Wärtsilä […]

Onsite Crack Repair | Metal Lock | Metal Surgery

By RA Power Solutions |

It is surprising, but the fact is that the metal lock and metal surgery process successfully repairs cracks and damaged components manufactured from cast iron, aluminium, and cast steel. This process of Onsite Crack Repair Has replaced the old and conventional method of crack repair by welding. Crack repair by metal stitching and locking is […]

Crack Repair In Cast Iron | Aluminium | Cast Steel

By RA Power Solutions |

RA Power Solutions has repaired cracks and damaged engine blocks in a simple process. This achievement of repairing engine blocks, turbine casings, cylinder heads, and major parts of high-capacity engines is possible because of our experience in undertaking repairs of damaged and cracked casting by the metal lock and metal stitching process. The cast iron […]

CRACK REPAIR BY METAL STITCHING INSTEAD OF WELDING | 47 YEARS OF EXPERIENCE

By RA Power Solutions |

Metal stitching is a technology that is over 200 years old and now very well proven and established to undertake crack repair or damage to cast components manufactured out of cast iron or aluminium alloy. In some cases, crack repair is also possible in components made of bronze. RA Power Solutions as a repair company […]

CRACK REPAIR OF LARGE CAST IRON COMPONENT | 47+ YEARS OF EXPERTISE

By RA Power Solutions |

Accidents in the case of rotatory equipment are common. Again, it is observed that in the case of stationary heavy-duty machinery parts made out of cast iron or cast steel, cracks develop due to fatigue, casting defects, or mechanical failures. The misalignment of components, excessive vibration, or overload can also be one of the causes […]

Cracked Cast Iron Repair | Metal Stitching of Damaged Casting

By RA Power Solutions |

No engineering plant does not have welding equipment and qualified welders. In case of damage or development of cracks in heavy and large components, we have experienced that the first reaction of the factory manager or a ship engineer is to repair cracked damaged components by welding. In 90% of cases, welding repairs for cracks […]

Damaged Engine Block and Heavy Components Successfully Repaired

By RA Power Solutions |

RA Power Solutions was advised about an accident with the auxiliary engine Yanmar 6M220L-SN by a Greece-based company that we have been serving for the last 47 years. A Team of Two Technicians was sent on board the vessel, and the following main observation was made: The scope of work included the following: Action taken […]

Cast Iron and Aluminium Components | Cold Metal Stitching

By RA Power Solutions |

Metal stitching services for cracked or damaged cast iron components are offered by RA Power Solutions. It is a very well-established and proven method used for the repair of cracks developed in heavy cast iron or Aluminium components. In fact, with our experience of forty-seven years in the field of repair of heavy engines and mechanical […]

Blog